Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultramid® B3ZG3 - PA6-I-GF15 - BASF

Material Data Center offers the following functions for Ultramid® B3ZG3:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, parameters for material models, CAE Interfaces

Check here, which other Ultramid B datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 模塑测量的特殊性能 - 加工推荐（注塑） - 函数
Any use of this information falls under the rules of our disclaimer.
材料文字说明
ULT. B3ZG3兼具韧性与结构强度，耐热性，耐化学性，易加工，易染色，因此在注塑加工后拥有优异的表面，适合各类消费品的应用，比如美发护发配件。
加工/物理特性干 / 已调节单位Test Standard
ISO数据
熔体体积流动速度, MVR 35 / * cm³/10min ISO 1133
温度 275 / * °C -
载荷 5 / * kg -
模塑收缩率, 平行 0.6 / * % ISO 294-4, 2577
模塑收缩率, 垂直 0.7 / * % ISO 294-4, 2577
机械性能干 / 已调节单位Test Standard
ISO数据
拉伸模量 5100 / 2900 MPa ISO 527
断裂应力 100 / 60 MPa ISO 527
断裂伸长率 5.3 / 18 % ISO 527
无缺口简支梁冲击强度, +23°C 75 / 110 kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C 55 / - kJ/m² ISO 179/1eU
简支梁缺口冲击强度, +23°C 16 / 30 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C 7 / - kJ/m² ISO 179/1eA
热性能干 / 已调节单位Test Standard
ISO数据
熔融温度, 10°C/min 220 / * °C ISO 11357-1/-3
热变形温度, 1.80 MPa 180 / * °C ISO 75-1/-2
热变形温度, 0.45 MPa 200 / * °C ISO 75-1/-2
线性热膨胀系数, 平行 35 / * E-6/K ISO 11359-1/-2
线性热膨胀系数, 垂直 129 / * E-6/K ISO 11359-1/-2
1.5mm名义厚度时的燃烧性 HB / * class IEC 60695-11-10
测试用试样的厚度 1.6 / * mm -
Yellow Card 现存 是的 / * - -
厚度为h时的燃烧性 HB / * class IEC 60695-11-10
测试用试样的厚度 0.7 / * mm -
Yellow Card 现存 是的 / * - -
电性能干 / 已调节单位Test Standard
ISO数据
相对介电常数., 1MHz 3.7 / 6.2 - IEC 62631-2-1
介质损耗因子, 100Hz 250 / - E-4 IEC 62631-2-1
介质损耗因子, 1MHz 250 / 2000 E-4 IEC 62631-2-1
体积电阻率 1E13 / 1E10 Ohm*m IEC 62631-3-1
表面电阻率 * / 1E10 Ohm IEC 62631-3-2
相对漏电起痕指数 - / 600 - IEC 60112
其它性能干 / 已调节单位Test Standard
吸水性 7.5 / * % 类似ISO 62
吸湿性 2.4 / * % 类似ISO 62
密度 1220 / - kg/m³ ISO 1183
模塑测量的特殊性能干 / 已调节单位Test Standard
ISO数据
粘数 160 / * cm³/g ISO 307, 1157, 1628
加工推荐（注塑）价值单位Test Standard
预干燥-温度 80 °C -
预干燥-时间 4 h -
加工湿度 ≤0.15 % -
注塑熔体温度 270 - 290 °C -
模具温度 80 - 90 °C -
函数
粘度－剪切速度 , Ultramid® B3ZG3, PA6-I-GF15, BASF
剪切应力－剪切速度 , Ultramid® B3ZG3, PA6-I-GF15, BASF
动态剪切模量－温度 , Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
应力－应变. , Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
应力－应变. , Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
正割模量－应变. , Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
正割模量－应变. , Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
应力－应变(等时的) 23°C, Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
蠕变模量－时间. 23°C, Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
蠕变曲线 23°C, Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
应力－应变(等时的) 90°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变模量－时间. 90°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变曲线 90°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
应力－应变(等时的) 120°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变模量－时间. 120°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变曲线 120°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
应力－应变(等时的) 160°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变模量－时间. 160°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
蠕变曲线 160°C, Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
比容－温度(pvT) , Ultramid® B3ZG3, PA6-I-GF15, BASF
拉伸模量－温度 , Ultramid® B3ZG3 (烘干), PA6-I-GF15, BASF
拉伸模量－温度 , Ultramid® B3ZG3 (状况), PA6-I-GF15, BASF
典型数据
加工方法
注塑
供货形式
粒料
添加剂
润滑剂, 脱模助剂
特殊性能
高冲击韧性的/经抗冲改性的, 经热稳处理的/耐热的
地区供应
北美, 欧洲, 亚太, 中南美洲, 中东/非洲
其他信息
注塑成型
PREPROCESSING
Pre/Post-processing, max. allowed water content: .15 %
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 4 h

PROCESSING
injection molding, Melt temperature, range: 270 - 290 °C
injection molding, Melt temperature, recommended: 280 °C
injection molding, Mold temperature, range: 80 - 90 °C
injection molding, Mold temperature, recommended: 80 °C
injection molding, Dwell time, thermoplastics: 10 min
耐化学性
酸类
醋酸 (5g/100g) (23°C)
柠檬酸溶液 (10g/100g) (23°C)
乳酸 (10g/100g) (23°C)
盐酸 (36g/100g) (23°C)
硝酸 (40g/100g) (23°C)
硫酸 (38g/100g) (23°C)
硫酸 (5g/100g) (23°C)
铬酸溶液 (40g/100g) (23°C)
碱类
氢氧化钠溶液 (35g/100g) (23°C)
氢氧化钠溶液 (1g/100g) (23°C)
醇类
异丙醇 (23°C)
甲醇 (23°C)
乙醇 (23°C)
碳氢化合物
正乙烷 (23°C)
甲苯 (23°C)
异辛烷 (23°C)
酮类
丙酮 (23°C)
醚类
(二)乙醚 (23°C)
矿物油
SAE 10W40号多效润滑油 (23°C)
SAE 10W40号多效润滑油 (130°C)
标准燃油
柴油(优先使用F类ISO 1817液体) (23°C)
柴油(优先使用F类ISO 1817液体) (>90°C)
盐溶液
氯化钠溶液(10g/100g) (23°C)
次氯化钠溶液 (10g/100g) (23°C)
氯化锌溶液 (50g/100g) (23°C)
其它
乙酸乙酯 (23°C)
过氧化氢 (23°C)
DOT4号刹车油 (130°C)
乙二醇水溶液 (50g/100g) (108°C)
水 (23°C)
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.